Effect of Composition on the Dielectric Properties of Electrical Porcelain.
The effect of compositional change on the dielectric properties (i.e. dielectric constant, dielectric resistance, dissipation factor, loss factor) of Electrical Porcelain has been investigated. The evaluation was carried out using six different compositions. The capacitance and resistance of the sam...
Đã lưu trong:
| Tác giả chính: | |
|---|---|
| Tác giả khác: | |
| Định dạng: | Luận văn |
| Ngôn ngữ: | Tiếng Anh |
| Được phát hành: |
Obafemi Awolowo University
2014
|
| Những chủ đề: | |
| Truy cập trực tuyến: | http://localhost:8080/xmlui/handle/123456789/2096 |
| Các nhãn: |
Thêm thẻ
Không có thẻ, Là người đầu tiên thẻ bản ghi này!
|
| Tóm tắt: | The effect of compositional change on the dielectric properties (i.e. dielectric constant, dielectric resistance, dissipation factor, loss factor) of Electrical Porcelain has been investigated. The evaluation was carried out using six different compositions. The capacitance and resistance of the samples of the six different compositions over a frequency range of 10 to 105 Hertz were measured. From these experimentally obtained values of resistance and capacitance, the values of the dielectric properties mentioned above were calculated.
The samples of the six different compositions were compacted under four different compaction pressures: 2.2 x 108 N/m2, 3.0 x 108 N/m2, 3.2 x 108 N/m2 and 3.5 x 108 N/m2, and fired at four different temperatures: 1250°C, 1300°C, 1350°C and 14000C, and the samples were of varying thicknesses ranging from 2.5mm to 8mm.
Available information from the present work suggest that sample “C” with composition, Kaolin, 39.25%; Feldspar, 24.50%; and Quartz, 36.25% gives the best dielectric properties of all the six different compositions. The most probable firing temperature, so as to avoid over firing as well as allow for dense formation to give good dielectric properties of the wares produced, is 1350°C. |
|---|